Complexes in polymers IV. FTIR microscopic characterization of thin organic polymer films containing embedded transition-metal carbonyl complexes

Thin films of polystyrene (PS), poly(methyl methacrylate) (PMMA) and polystyrene-polyacrylonitrile copolymer (PS-AN), containing various embedded transition-metal complexes, have been studied by FTIR microscopy. The spatial distributions of the transition-metal carbonyl complexes throughout the thin organic polymer films have been determined by a two-dimensional IR mapping procedure. The spectral variations observed in the distribution of the metal carbonyls throughout the different polymer films are discussed. The IR data show that the technique used to prepare the organometallic-embedded thin films (viz. freeze-drying of solutions followed by hot mechanical pressing of the residues) does in general lead to homogeneous films which may eventually find industrial application, e.g. as membrane sensors for small molecules.     

Electron microscopy study of aggregation of microclusters of sulphur

A study of aggregation of sulphur particles in colloidal suspension of sulphur in water-methanol mixture using TEM and electron diffraction is reported. From the micrographs the aggregates formed have been found to be random and tenuous indicating a fractal structure. The electron diffraction patterns of the aggregates are used to study the mechanism of diffusion and reaction limited aggregation.     

AFM, SEM and GIXRD studies of thin films of red polycarbazolyldiacetylenes

In this paper we report the results of a morphological and structural investigation on film properties of a soluble polydiacetylene, the poly[1,6-bis(3,6-dihexadecyl-N-carbazolyl)-2,4-hexadiyne] (polyDCHD-HS). The red films of this polymer, prepared by standard spin-coating techniques, revealed absence of linear dichroism and birefringence in contrast with the ordered mesophases detected by powder X-ray studies. In order to interpret the optical behavior of this polymer, we performed AFM and SEM studies of polyDCHD-HS films spun on hydrophylic and hydrophobic glass substrates. We found the presence of surfaces organized in rod-like particles, more regularly oriented on the hydrophylic substrate. GIXRD studies, carried out on films sufficiently thick to allow the observation of the diffraction pattern, reveled the presence of a lamellar structure with a spacing of 3.22 nm. The low intensity of the diffraction peaks and the isotropic linear optical properties of the films show that the lamellar mesophases are not extended over large areas. These findings were compared with the data obtained from AFM and SEM studies on films of two other polydiacetylenes, the poly[1-(3,6-dihexadexyl-N-carbazolyl)-6-(N-carbazolyl)-2,4-hexadyine] (polya-DCHD) and the poly[1,6-bis(3,6-dipalmitoyl-N-carbazolyl)-2,4-hexadyine] (polyDPCHD), spun on hydrophylic glass substrate. The results confirmed the presence of nodular morphologies which seem to be a general characteristic of this class of materials. The particles organization appears instead related to the chemical nature of the substituents on the carbazolyl rings.     

Front roughening in three-dimensional imbibition

We investigate the structure and dynamics of the interface between two immiscible liquids in a three-dimensional disordered porous medium. We apply a phase-field model that includes explicitly disorder and discuss both spontaneous and forced imbibition. The structure of the interface is dominated by a length scale ξ_× which arises from liquid conservation. We further show that disorder in the capillary and permeability act on different length scales and give rise to different scalings and structures of the interface properties. We conclude with a range of applications.     

Study of intermediates formed in the oxidation of thiols

The oxidation of aminoethanethiol (1) was investigated in acid solutions on a glass carbon anode. It was shown that at relatively low anode potentials thiyl radicals RS^· are released into the solution, but this does not lead to binding of the oxygen in the solution. Raising the anode potential leads to binding of oxygen, which is probably due to the formation of the intermediate RS⁺. The oxidation of 1 was studied in Ce(SO₄)₂+H₂SO₄ solution. It was shown that under certain conditions the intermediate is RS⁺, which subsequently converts to a product that could not be identified as any previously described product of the oxidation of thiols. Proposals are made regarding its structure and conversion pathways.B. P. Konstantinov Institute of Nuclear Physics, Russian Academy of Sciences, 188350 Leningrad. Translated from Izvestiya Akademii Nauk, Seriya Khimicheskaya, No. 2, pp. 278–288, February, 1992.     

Scanning probe microscopy studies of PbS surfaces oxidized in air and etched in aqueous acid solutions

Natural n-type PbS single crystals have been studied using AFM, STM and STS after long-term oxidation in air at ambient temperatures and extensive etching in aqueous acid solutions, in contrast to previous work devoted to initial corrosion of fresh surfaces. The exposure of PbS to atmosphere at high relative humidity for several days yields widespread loose oxidation products; the process is much slower at low humidity. Surface morphologies diverge after the treatment in 1 M perchloric and hydrochloric acid solutions at room temperature and become widely different at elevated temperatures, displaying commonly etch pits up to several micrometers in size and depth along with rather uniformly distributed 20-100 nm protrusions of PbS phase. The changes both in topography and semiconducting properties of PbS found by tunneling spectroscopy have been explained in terms of the non-uniform distribution of donor- and acceptor-type defects D⁺/D⁻ in the metal depleted surface layer, which are generated by chemical reactions and, in turn, determine the rates of the PbS corrosion. In particular, the D⁻ centers exhibit a self-catalyzing effect on the non-oxidative local dissolution of PbS in HCl media, resulting in the deep etch pits.     

杀菌剂福美双的电化学性质及线性扫描溶出伏安法测定

提出了线性扫描溶出伏安法测定福美双的电分析化学方法.在 pH 5.0 HAc-NaAc缓冲溶液中福美双在汞电极上出现一还原峰,峰电位为-610 mV(vs.Ag/AgCl).采用各种电化学技术如循环伏安法和线性扫描溶出伏安法等对本体系进行研究,发现采用线性扫描溶出伏安法能得到较灵敏的还原峰,呈现不可逆电极反应现象,并具有一定的吸附性,在210 s时能达到吸附平衡.选择吸附时间为180 s时,线性范围为0.02～0.14 μg·mL-1,最低检测限为9.5 ng·mL-1.将本方法用于实际样品的测定,得到满意的结果.     

Adhesion studies of latex film surfaces on the meso- and nanoscale

In this paper the effects of surface roughness and annealing temperature (T) of latex coating films on adhesion are discussed for the different stages of the film formation process. The surface free energy of latex films was assessed in terms of practical work of adhesion (W) (or adherence) using a custom-built adhesion-testing device (ATD), atomic force microscopy (AFM), and contact angle measurements. For preannealed latex films surface roughness averages (R_a) were determined from AFM height images and were related to the values of W obtained from ATD measurements at room temperature. The results obtained using these tests exhibiting surface behavior on different length scales indicate a dependence of the measured adhesion on surface roughness and temperature, as well as on the length scale of the measurements.First preannealed samples were studied, which were obtained by heat treatment above the respective glass transition temperatures (T_g). Increasing the temperature of preannealing resulted in a decrease of the adherence observed in ATD experiments at room temperature. However, on the nanoscale, using AFM, no significant variation of the adherence was observed. This observation can be explained by roughness arguments. Preannealing decreases roughness which results in lower adherence values measured by ATD while for essentially single asperity AFM experiments roughness has an insignificant effect. Specimens were also annealed over a constant period of time (90 min) at different temperatures. At the end of the heat treatment, adhesion was measured at the treatment temperature by ATD. The amplified effect of temperature observed in this case on adherence is attributed to the combination of roughness decrease and increasing test temperature. In a third set of experiments completely annealed samples were studied by ATD as well as by AFM as a function of temperature. With increasing T values ATD showed a decrease in adherence, which is attributed to a decreasing surface free energy of the annealed films at elevated T values. AFM, on the other hand, showed an opposite trend which is assigned to increasing penetration of the tip into the tip/wetting polymer samples versus increasing temperature. Finally, annealing isotherms as a function of time were investigated by ATD in situ at different temperatures. This last set of experiments allowed us to optimize annealing time and temperature to achieve complete curing.     

Impact of 100 MeV Au on the surface of relaxed Si0.5Ge0.5 alloy films studied by atomic force microscopy

We demonstrate a gradual surface modification process of relaxed Si_0.5Ge_0.5 alloy films by 100 MeV Au beam with fluence varying between 5 × 10¹⁰ and 1 × 10¹² ions/cm² at 80 K by means of atomic force microscopy (AFM). Presence of Ge quantum dots (QDs) was found in the virgin sample. The disappearance of the QDs were noticed when the samples were irradiated with a fluence of 5 × 10¹⁰ ions/cm². Craters were found developing at a fluence of 1 × 10¹¹ ions/cm². Apart from the evolution of the craters, blisters were also detected at a fluence of 1 × 10¹² ions/cm². Variation of the average root mean square value of the surface roughness as a function of fluence was examined.